Method for controlling concentration of donor in GA2O3—based single crystal

ABSTRACT

A method for controlling the concentration of a donor in a Ga 2 O 3 -based single crystal includes: a step in which a Group IV element is implanted as a donor impurity in a Ga 2 O 3 -based single crystal by ion implantation process to form, in the Ga 2 O 3 -based single crystal, a donor impurity implantation region that has a higher concentration of the Group IV element than the region in which the Group IV element has not been implanted; and a step in which annealing at 800 C or higher is conducted to activate the Group IV element present in the donor impurity implantation region and thereby form a high-donor-concentration region. Thus, the donor concentration in the Ga 2 O 3 -based single crystal is controlled.

TECHNICAL FIELD

The invention relates to a method for controlling a concentration of a donor in a Ga₂O₃-based single crystal and, in particular, to a method for controlling the concentration of a donor in a Ga₂O₃-based single crystal using ion implantation process.

BACKGROUND ART

As a conventional method of forming a Ga₂O₃ single crystal, a method is known in which a Group IV element such as Si or Sn is added while growing a Ga₂O₃ single crystal to impart conductivity to the Ga₂O₃ single crystal (see, e.g., PTL 1).

Meanwhile, as another conventional method of forming a Ga₂O₃ single crystal, a method is known in which a β-Ga₂O₃ crystal is heteroepitaxially grown on a sapphire substrate while adding an impurity such as Sn to form a β-Ga₂O₃ crystal film having conductivity (see, e.g., PTL 2).

A method in which an impurity ion is introduced into a SiC crystal by ion implantation process is also known (see, e.g., PTL 3).

CITATION LIST Patent Literature

[PTL 1]

JP-A 2005-235961

[PTL 2]

Japanese Patent No. 4083396

[PTL 3]

Japanese Patent No. 4581270

SUMMARY OF INVENTION Technical Problem

In the meantime, it is difficult to use the ion implantation process to introduce an impurity into an oxide single crystal such as Ga₂O₃ single crystal for the purpose of imparting conductivity. This is because the oxide is likely to be damaged by ion implantation and such damage is difficult to be sufficiently repaired even if annealing treatment is perfoimed after the ion implantation. It is believed that, in the oxide single crystal, oxygen deficiency during the ion implantation increases damage on the crystal.

However, the ion implantation process is advantageous in that, e.g., an impurity concentration can be controlled after forming a base crystal or it is possible to locally introduce an impurity relatively easily.

It is an object of the invention to provide a method for controlling the concentration of a donor in a Ga₂O₃-based single crystal using ion implantation process that allows the formation of a highly electrically conductive region in a Ga₂O₃-based single crystal.

Solution to Problem

According to one embodiment of the invention, a method for controlling a concentration of a donor in a Ga₂O₃-based single crystal as defined in [1] to [5] below is provided so as to achieve the above object.

[1] A method for controlling a concentration of a donor in a Ga₂O₃-based single crystal, comprising:

-   -   a step of introducing a Group IV element as a donor impurity         into a Ga₂O₃-based single crystal by ion implantation process so         as to form a donor impurity implantation region having a higher         concentration of the Group IV element than the region without         implanting the Group IV element in the Ga₂O₃-based single         crystal; and     -   a step of activating the Group IV element present in the donor         impurity implantation region by annealing treatment at a         temperature not less than 800° C. to form a         high-donor-concentration region.

[2] The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to [1], wherein the annealing treatment is conducted under a condition of not less than 800° C. in a nitrogen atmosphere.

[3] The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to [1], wherein the annealing treatment is conducted under a condition of not less than 800° C. and not more than 950° C. in an oxygen atmosphere.

[4] The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to one of [1] to [3], wherein the Group IV element is introduced into a partial region of a surface of the Ga₂O₃-based single crystal using a mask formed on the Ga₂O₃-based single crystal so as to form the donor impurity implantation region in the partial region of the surface of the Ga₂O₃-based single crystal.

[5] The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to [1], wherein the Ga₂O₃-based single crystal comprises a Ga₂O₃-based single crystal substrate or a Ga₂O₃-based crystal film formed on a supporting substrate.

Advantageous Effects of Invention

According to an embodiment of the invention, a method for controlling the concentration of a donor in a Ga₂O₃-based single crystal using ion implantation process can be provided that allows the formation of a highly electrically conductive region in a Ga₂O₃-based single crystal.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1A is a cross sectional view of a β-Ga₂O₃-based crystal, showing an example of ion implantation process.

FIG. 1B is a cross sectional view of the β-Ga₂O₃-based crystal, showing the example of ion implantation process.

FIG. 1C is a cross sectional view of the β-Ga₂O₃-based crystal, showing the example of ion implantation process.

FIG. 1D is a cross sectional view of the β-Ga₂O₃-based crystal, showing the example of ion implantation process.

FIG. 2 is a graph showing a relation between annealing treatment temperature in a nitrogen atmosphere after ion implantation and conductivity of a β-Ga₂O₃ crystal film.

FIG. 3 is a graph showing a relation between annealing treatment temperature in an oxygen atmosphere after ion implantation and conductivity of a β-Ga₂O₃ crystal film.

DESCRIPTION OF EMBODIMENTS Embodiment

According to the present embodiment, introduction of a donor impurity into a Ga₂O₃-based single crystal using the ion implantation process and subsequent annealing treatment performed under predetermined conditions allow a high-donor-concentration region having superior electrical conductivity to be formed in the Ga₂O₃-based crystal. Following is an embodiment thereof and a method for controlling the concentration of a donor in a β-Ga₂O₃-based single crystal will be described in detail as an example. It should be noted that the Ga₂O₃-based single crystal in the present embodiment is not limited to a β-Ga₂O₃-based single crystal and may be a Ga₂O₃-based single crystal having another structure such as α-Ga₂O₃-based single crystal.

FIGS. 1A to 1D are cross sectional views of a β-Ga₂O₃-based crystal, showing an example of ion implantation process.

Firstly, a mask 2 is formed on a β-Ga₂O₃-based single crystal 1, as shown in FIG. 1A. The mask 2 is formed using a photolithography technique, etc.

Next, as shown in FIG. 1B, a donor impurity is implanted into the β-Ga₂O₃-based single crystal 1 by ion implantation and a donor impurity implantation region 3 is thereby formed on a surface of the β-Ga₂O₃-based single crystal 1. At this point, since the donor impurity is not implanted into a region of the β-Ga₂O₃-based single crystal 1 covered with the mask 2, the donor impurity implantation region 3 is formed in a partial region of the surface of the β-Ga₂O₃-based single crystal 1. The donor impurity concentration in the donor impurity implantation region 3 is higher than that of the β-Ga₂O₃-based single crystal 1 in the region with no impurity implanted.

Alternatively, the donor impurity implantation region 3 may be formed on the entire surface of the β-Ga₂O₃-based single crystal 1 by ion implantation without using the mask 2. In addition, it is possible to control depth or concentration distribution of the donor impurity implantation region 3 by adjusting the ion implantation conditions.

Next, the mask 2 is removed, as shown in FIG. 1C.

After that, the donor impurity in the donor impurity implantation region 3 is activated by performing annealing treatment at not less than 800° C., thereby forming a high-donor-concentration region 4 having a high donor concentration, as shown in FIG. 1D. In addition, damage on the β-Ga₂O₃-based single crystal 1 caused by the ion implantation can be repaired by this annealing treatment. In detail, the annealing treatment conditions are, e.g., not less than 800° C. in an inert atmosphere such as nitrogen atmosphere or argon atmosphere, or not less than 800° C. and not more than 950° C. in an oxygen atmosphere.

The β-Ga₂O₃-based single crystal 1 is constructed from a β-Ga₂O₃ single crystal or a β-Ga₂O₃ single crystal doped with elements such as Al and In. It may be, e.g., a (Ga_(x)Al_(y)In_((1-x-y)))₂O₃ (0<x≦1, 0≦y≦1, 0<x+y≦1) crystal which is a β-Ga₂O₃ crystal doped with Al and In. The band gap is widened by adding Al and is narrowed by adding In.

The β-Ga₂O₃-based single crystal 1 is a β-Ga₂O₃-based single crystal substrate or a β-Ga₂O₃-based crystal film formed on a supporting substrate.

Group IV elements such as Si, Sn and Ge are used as a donor impurity to be introduced into the β-Ga₂O₃-based single crystal 1 by the ion implantation process.

FIG. 2 is a graph showing a relation between annealing treatment temperature in a nitrogen atmosphere after ion implantation and conductivity of the β-Ga₂O₃ single crystal substrate as the β-Ga₂O₃-based single crystal. The vertical axis in FIG. 2 indicates a difference between donor density and acceptor density (Nd—Na) per unit cubic centimeter in the high-donor-concentration region of the β-Ga₂O₃ single crystal substrate, i.e., indicates a conductivity level of the high-donor-concentration region of the β-Ga₂O₃ single crystal substrate which is an n-type semiconductor. The horizontal axis in FIG. 2 indicates annealing treatment temperature in a nitrogen atmosphere. The annealing treatment is performed for 30 minutes each.

The high-donor-concentration region is a box-shaped region having a depth of 200 nm and is formed by ion-implanting Si or Sn with a concentration of 1×10¹⁹/cm³ into a β-Ga₂O₃ single crystal substrate having a donor concentration of 3×10¹⁷/cm³. In addition, the high-donor-concentration region is formed by vertically implanting a donor impurity on a (010) plane, as a main surface, of the β-Ga₂O₃ single crystal substrate.

The filled square and the filled triangle in FIG. 2 indicate Nd—Na values when respectively implanting Si and Sn as a donor impurity. Meanwhile, the open circle indicates Nd—Na values when the donor impurity is not implanted.

As shown in FIG. 2, the Nd—Na value is increased by annealing treatment at not less than 800° C. in case of implanting Si as well as in case of implanting Sn. That is, the annealing treatment at not less than 800° C. in a nitrogen atmosphere after the ion implantation allows high conductivity to be imparted to the β-Ga₂O₃ single crystal substrate. It should be noted that, when the donor impurity is not implanted, the Nd—Na value is not greatly increased even if the annealing treatment temperature is raised.

FIG. 3 is a graph showing a relation between annealing treatment temperature in an oxygen atmosphere after ion implantation and conductivity of the β-Ga₂O₃ single crystal substrate as the β-Ga₂O₃-based single crystal. The vertical axis in FIG. 3 indicates a difference between donor density and acceptor density (Nd—Na) per unit cubic centimeter in the high-donor-concentration region of the β-Ga₂O₃ single crystal substrate, i.e., indicates a conductivity level of the high-donor-concentration region of the β-Ga₂O₃ single crystal substrate which is an n-type semiconductor. The horizontal axis in FIG. 3 indicates annealing treatment temperature in an oxygen atmosphere. The annealing treatment is performed for 30 minutes each.

The filled square and the filled triangle in FIG. 3 indicate the Nd—Na values when respectively implanting Si and Sn as a donor impurity.

As shown in FIG. 3, the Nd—Na value is increased by annealing treatment at not less than 800° C. and not more than 950° C. when Si is implanted. Also, the Nd—Na value is increased by annealing treatment at not less than 800° C. and not more than 1100° C. when Sn is implanted. That is, the annealing treatment at not less than 800° C. and not more than 950° C. in an oxygen atmosphere after the ion implantation allows high conductivity to be imparted to the β-Ga₂O₃ single crystal substrate.

Effects of the Embodiment

According to the present embodiment, introduction of a donor impurity into a β-Ga₂O₃-based crystal using the ion implantation process and subsequent annealing treatment perfoimed under predetermined conditions allow a high-donor-concentration region having superior electrical conductivity to be formed in the β-Ga₂O₃-based crystal. Since the high-donor-concentration region is formed using the ion implantation process, it is possible to control the donor concentration in the high-donor-concentration region after forming the β-Ga₂O₃-based crystal and thereby to impart a desired conductivity. In addition, use of a mask, etc., allows the high-donor-concentration region to be locally formed in the β-Ga₂O₃-based crystal.

Although the embodiment the invention has been described above, the invention according to claims is not to be limited to the above-mentioned embodiment. Further, it should be noted that all combinations of the features described in the embodiment are not necessary to solve the problem of the invention.

INDUSTRIAL APPLICABILITY

A method for controlling the concentration of a donor in a Ga₂O₃-based single crystal using ion implantation process, which allows a highly electrically conductive region to be formed in a Ga₂O₃-based single crystal, is provided.

REFERENCE SIGNS LIST

-   1: β-Ga₂O₃-based single crystal -   2: mask -   3: donor impurity implantation region -   4: high-donor-concentration region 

The invention claimed is:
 1. A method for controlling a concentration of a donor in a Ga₂O₃-based single crystal, comprising: introducing a Group IV element as a donor impurity into a Ga₂O₃-based single crystal by ion implantation process so as to form a donor impurity implantation region having a higher concentration of the Group IV element than a region without implanting the Group IV element in the Ga₂O₃-based single crystal; and activating the Group IV element present in the donor impurity implantation region by annealing treatment at a temperature not less than 800° C. to form a high-donor-concentration region.
 2. The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to claim 1, wherein the annealing treatment is conducted under a condition of not less than 800° C. in a nitrogen atmosphere.
 3. The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to claim 1, wherein the annealing treatment is conducted under a condition of not less than 800° C. and not more than 950° C. in an oxygen atmosphere.
 4. The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to claim 1, wherein the Group IV element is introduced into a partial region of a surface of the Ga₂O₃-based single crystal using a mask formed on the Ga₂O₃-based single crystal so as to form the donor impurity implantation region in the partial region of the surface of the Ga₂O₃-based single crystal.
 5. The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to claim 1, wherein the Ga₂O₃-based single crystal comprises a Ga₂O₃-based single crystal substrate or a Ga₂O₃-based crystal film formed on a supporting substrate.
 6. The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to claim 2, wherein the Group IV element is introduced into a partial region of a surface of the Ga₂O₃-based single crystal using a mask formed on the Ga₂O₃-based single crystal so as to form the donor impurity implantation region in the partial region of the surface of the Ga₂O₃-based single crystal.
 7. The method for controlling a concentration of a donor in a Ga₂O₃-based single crystal according to claim 3, wherein the Group IV element is introduced into a partial region of a surface of the Ga₂O₃-based single crystal using a mask formed on the Ga₂O₃-based single crystal so as to form the donor impurity implantation region in the partial region of the surface of the Ga₂O₃-based single crystal. 